UL 3266
| HOOK-UP WIRE | UL 3266 | ||||
 |
Product Construction 產(chǎn)品結(jié)構(gòu) | ||||
| Conductor 導(dǎo)體 |
Material 材料 | Tinned Copper 鍍錫銅絲 | |||
| AWG 線規(guī) | 18 | ||||
| Conductors No 導(dǎo)體數(shù) | 41 | ||||
| Diameter 規(guī)格(mm) | 0.16 | ||||
| Jacket 護套 |
Material 材料 | XL-PVC | |||
| Average Thickness 平均厚度(mm) | 0.50 | ||||
| Minimun Thickness 最小厚度(mm) | 0.43 | ||||
| Diameter 線徑(mm) | 2.18 | ||||
| Product Standard 產(chǎn)品標(biāo)準(zhǔn) | |||||
| Rated Temperature 額定溫度（℃） |
125 | ||||
| Rated Voltage 額定電壓（V） |
300 | ||||
| Product Standard Certification | E308941 | ||||
| Passes UL VW-1 & CSA FT1 vertical flame test 通過UL VW-1 & CSA FT1垂直耐燒測試 |
|||||
| Reference Standard | UL 758 UL 1581 | ||||
| Printing 印字 | |||||
AMCOWRE E308941  AWM STYLE 3266 18AWG 125℃ 300V VW-1 --- c AWM 1 A/B 125℃ 300V FT1 -F- -LF- ROHS S&Y |
|||||
| Mechanical Characteristic 物理機械性能 | |||||
| Testing Object 檢測對象 | Jacket Material 護套料 | ||||
| Testing Material 實驗材料 | XL-PVC | ||||
| Aging Condition 老化條件（℃*hrs） | 158*168 | ||||
| Befor Aging 老化前 |
Tensile Strength 抗張強度（Mpa） | >=1.05 | |||
| Elongation伸長率(%) | >=100 | ||||
| After Aging 老化后 |
Tensile Strength 抗張強度(Mpa) | >=70% of unaged | |||
| Elongation伸長率(%) | >=65% of unaged | ||||
| AWG 線規(guī) |
Conductor No./mm 導(dǎo)體數(shù)/線徑（mm） |
Jacket Diameter 護套線徑（mm） |
Jacket Average Thickness 平均厚度（mm） |
Jacket Minimum Thickness 最小厚度（mm） |
Weight 重量 |
| 16 | 26/0.16 | 2.46 | 0.50 | 0.43 | 16.50 |
| 18 | 41/0.16 | 2.18 | 0.50 | 0.43 | 11.41 |
| 20 | 26/0.16 | 1.93 | 0.42 | 0.36 | 7.61 |
| 22 | 17/0.16 | 1.60 | 0.42 | 0.36 | 5.37 |
| 24 | 11/0.16 | 1.37 | 0.42 | 0.36 | 3.68 |
| 26 | 7/0.16 | 1.28 | 0.42 | 0.36 | 3.08 |
| 28 | 7/0.127 | 1.20 | 0.42 | 0.36 | 2.28 |